Cupro Nickel Pipe For Heat Exchangers, Cupro Nickel Pipe For Sea Water Pipeline, Manufacturer and exporter from India,
C70600 , Cupro nickel offers excellent corrosion resistance, especially in marine salt water environments. The main, wrought Cupro Nickel alloys chosen for sea water service contain 10 or 30 percent nickel. They also have important additions of iron and manganese which are necessary to maintain good corrosion resistance.
AUTOMOTIVE: Power Steering Tube, Brake Lines
CONSUMER: Screw Lamp Bases
INDUSTRIAL: Condenser Plates, Condensers, Weld Torch Tips, Heat Exchanger Tubes, Valve Bodies, Evaporator Tubes, Pressure Vessels, Distiller Tubes, Pump Impellers for Oil Refining, Ferrules, Evaporators
MARINE: Boat Hulls, Tube Sheet for Salt Water Service, Salt Water Pipe Fittings, Salt Water Piping Systems, Salt Water Piling Wrap, Hot Water Tanks, Salt Water Baffles, Propeller Sleeves, Ship Hulls, Water Hoses
PLUMBING: Flanges
| SPECIFICATIONS | DESIGNATION |
| ISO | CuNi10Fe1Mn |
| Europen | CuNi10Fe1Mn |
| BS | CN 102 |
| JIS | C 7060 |
| Russian | MNZMo10-1-1 |
| Cu | Fe | Pb | Mn | Ni | Zn | |
| Min/Max | Rem | 1.0 – 1.8 | 0.05 | 1 | 9.0 – 11.0 | 1 |
| Nominals | 88.6000 | 1.4000 | – | – | 10.0000 | – |
| Product Property | US Customary |
| Coefficient Of Thermal Expansion | 9.5 10−6Per °F (68-572 F) |
| Density | 0.323 Lb/In3 At 68 F |
| Electrical Conductivity | 9 %IACS @ 68 F |
| Electrical Resistivity | 115.0 Ohms-Cmil/Ft @ 68 F |
| Melting Point – Liquidus | 2100 F |
| Melting Point – Solidus | 2010 F |
| Modulas Of Elasticity In Tension | 18000 Ksi |
| Modulus Of Rigidity | 6800 Ksi |
| Specific Gravity | 8.94 |
| Specific Heat Capacity | 0.09 Btu/Lb/°F At 68 F |
| Thermal Conductivity | 26.0 BTU In/Hr.Ft2.°F @ 68 F |
| WIRE | 1mm To 8mm |
| HOLLOW RODS | Min Bore Size 20 Mm And Max OD 100 Mm |
| ROUND RODS/RODS | 8mm To 100 Mm |
| HEX | 10mm To 60mm |
| SQUARE | 10mm To 60mm |
| FLAT | 10mm Min Thickness And Max Width 120mm |
| BILLETS | Up To 200 Mm |
| INGOTS | AS Per Specification |
Excellent hot and cold workability; good forge ability. Fabricated by bending, coining, coppersmith, drawing and upsetting, hot forging and pressing, knurling, roll threading, shearing, spinning, swaging, and stamping.
Good to excellent. Susceptible to galvanic corrosion when coupled with iron, aluminum, magnesium, leads, tin, and zinc. Good resistance to atmospheric, brackish water, sea water, and non-oxidizing acid corrosion, but avoid heating in oxidizing atmospheres or exposing to oxidizing acids, moist halogens, sulfides, ammonia, or solutions with ammonium ions.
Industrial: Condensers ,Condenser Plates, Evaporator Tubes , Ferrules , Heat Exchanger Tubes, Corrosion Resistanc Corrosion Resistanc, Petrochemicals, Salt Water, Erosion and Impingement, Moderate Strength, Retains Strength at High Temperatures
Marine: Condenser Intake Systems , Salt Water Piping
| SPECIFICATIONS | DESIGNATION |
| ISO | CuNi5Fe1Mn |
| BS | CN 101 |
| Russian | MNZ5-1 |
| Cu | Fe | Pb | Mn | Ni | Zn | |
| Min/Max | Rem | 1.3 – 1.7 | 0-.05 | 0.3-0.8 | 4.8 €“ 6.2 | 0-1.0 |
| Melting Point – Liquidus°F | 2050 |
| Densitylb/Cu In. At 68°F | 0.323 |
| Specific Gravity | 8.94 |
| Electrical Conductivity% IACS At 68°F | 14 |
| Thermal ConductivityBtu/ Sq Ft/ Ft Hr/ °F At 68°F | 37 |
| Coefficient Of Thermal Expansion 68-572 10−6Per °F (68-572 F) | 9.7 |
| Specific Heat CapacityBtu/Lb/°F At 68°F | 0.09 |
| Modulus Of Elasticity In Tensionksi | 17000 |
| Modulus Of Rigidityksi | 6400 |
| HOLLOW RODS | Min Bore Size 20 Mm And Max OD 100 Mm |
| ROUND RODS/RODS | 8mm To 100 Mm |
| HEX | 10mm To 60mm> |
| SQUARE | 10mm To 60mm |
| FLAT | 10mm Min Thickness And Max Width 120mm |
| BILLETS | Up To 200 Mm |
| INGOTS | AS Per Specification |
C70600 , Cupro nickel offers excellent corrosion resistance, especially in marine salt water environments. The main, wrought cupro nickel alloys chosen for sea water service contain 10 or 30 percent nickel. They also have important additions of iron and manganese which are necessary to maintain good corrosion.
AUTOMOTIVE: Power Steering Tube, Brake Lines
CONSUMER: Screw Lamp Bases
INDUSTRIAL: Condenser Plates, Condensers, Weld Torch Tips, Heat Exchanger Tubes, Valve Bodies, Evaporator Tubes, Pressure Vessels, Distiller Tubes, Pump Impellers for Oil Refining, Ferrules, Evaporators
MARINE: Boat Hulls, Tube Sheet for Salt Water Service, Salt Water Pipe Fittings, Salt Water Piping Systems, Salt Water Piling Wrap, Hot Water Tanks, Salt Water Baffles, Propeller Sleeves, Ship Hulls, Water Hoses
PLUMBING: Flanges
| SPECIFICATIONS | DESIGNATION |
| ISO | CuNi10Fe1Mn |
| Europen | CuNi10Fe1Mn |
| BS | CN 102 |
| JIS | C 7060 |
| Russian | MNZMo10-1-1 |
| Cu | Fe | Pb | Mn | Ni | Zn | |
| Min/Max | Rem | 1.0 – 1.8 | 0.05 | 1 | 9.0 – 11.0 | 1 |
| Nominals | 88.6000 | 1.4000 | – | – | 10.0000 | – |
| Product Property | US Customary |
| Coefficient Of Thermal Expansion | 9.5 10−6Per °F (68-572 F) |
| Density | 0.323 Lb/In3 At 68 F |
| Electrical Conductivity | 9 %IACS @ 68 F |
| Electrical Resistivity | 115.0 Ohms-Cmil/Ft @ 68 F |
| Melting Point – Liquidus | 2100 F |
| Melting Point – Solidus | 2010 F |
| Modulas Of Elasticity In Tension | 18000 Ksi |
| Modulus Of Rigidity | 6800 Ksi |
| Specific Gravity | 8.94 |
| Specific Heat Capacity | 0.09 Btu/Lb/°F At 68 F |
| Thermal Conductivity | 26.0 BTU In/Hr.Ft2.°F @ 68 F |
| HOLLOW RODS | Min Bore Size 20 Mm And Max OD 100 Mm |
| ROUND RODS/RODS | 8mm To 100 Mm |
| HEX | 10mm To 60mm> |
| SQUARE | 10mm To 60mm |
| FLAT | 10mm Min Thickness And Max Width 120mm |
| BILLETS | Up To 200 Mm |
| INGOTS | AS Per Specification |
Excellent hot and cold workability; good forge ability. Fabricated by bending, coining, coppersmith, drawing and upsetting, hot forging and pressing, knurling, roll threading, shearing, spinning, swaging, and stamping.
Good to excellent. Susceptible to galvanic corrosion when coupled with iron, aluminum, magnesium, leads, tin, and zinc. Good resistance to atmospheric, brackish water, sea water, and non-oxidizing acid corrosion, but avoid heating in oxidizing atmospheres or exposing to oxidizing acids, moist halogens, sulfides, ammonia, or solutions with ammonium ions.
Industrial: Condensers ,Condenser Plates, Evaporator Tubes , Ferrules , Heat Exchanger Tubes, Corrosion Resistanc Corrosion Resistanc, Petrochemicals, Salt Water, Erosion and Impingement, Moderate Strength, Retains Strength at High Temperatures.
Marine: Condenser Intake Systems , Salt Water Piping
| SPECIFICATIONS | DESIGNATION |
| ISO | CuNi5Fe1Mn |
| BS | CN 101 |
| Russian | MNZ5-1 |
| Cu | Fe | Pb | Mn | Ni | Zn | |
| Min/Max | Rem | 1.3 – 1.7 | 0.05 | 0.3-0.8 | 4.8 €“ 6.2 | 0-1.0 |
| Melting Point – Liquidus°F | 2050 |
| Densitylb/Cu In. At 68°F | 0.323 |
| Specific Gravity | 8.94 |
| Electrical Conductivity% IACS At 68°F | 14 |
| Thermal ConductivityBtu/ Sq Ft/ Ft Hr/ °F At 68°F | 37 |
| Coefficient Of Thermal Expansion 68-572 10−6Per °F (68-572 F) | 9.7 |
| Specific Heat CapacityBtu/Lb/°F At 68°F | 0.09 |
| Modulus Of Elasticity In Tensionksi | 17000 |
| Modulus Of Rigidityksi | 6400 |
| HOLLOW RODS | Min Bore Size 20 Mm And Max OD 100 Mm |
| ROUND RODS/RODS | 8mm To 100 Mm |
| HEX | 10mm To 60mm> |
| SQUARE | 10mm To 60mm |
| FLAT | 10mm Min Thickness And Max Width 120mm |
| BILLETS | Up To 200 Mm |
| INGOTS | AS Per Specification |
C70600 , Cupro nickel offers excellent corrosion resistance, especially in marine salt water environments. The main, wrought cupro nickel alloys chosen for sea water service contain 10 or 30 percent nickel. They also have important additions of iron and manganese which are necessary to maintain good corrosion resistance.
AUTOMOTIVE: Power Steering Tube, Brake Lines
CONSUMER: Screw Lamp Bases
INDUSTRIAL: Condenser Plates, Condensers, Weld Torch Tips, Heat Exchanger Tubes, Valve Bodies, Evaporator Tubes, Pressure Vessels, Distiller Tubes, Pump Impellers for Oil Refining, Ferrules, Evaporators
MARINE: Boat Hulls, Tube Sheet for Salt Water Service, Salt Water Pipe Fittings, Salt Water Piping Systems, Salt Water Piling Wrap, Hot Water Tanks, Salt Water Baffles, Propeller Sleeves, Ship Hulls, Water Hoses
PLUMBING: Flanges
| SPECIFICATIONS | DESIGNATION |
| ISO | CuNi10Fe1Mn |
| Europen | CuNi10Fe1Mn |
| BS | CN 102 |
| JIS | C 7060 |
| Russian | MNZMo10-1-1 |
| Cu | Fe | Pb | Mn | Ni | Zn | |
| Min/Max | Rem | 1.0 – 1.8 | 0.05 | 1 | 9.0 – 11.0 | 1 |
| Nominals | 88.6000 | 1.4000 | – | – | 10.0000 | – |
| Product Property | US Customary |
| Coefficient Of Thermal Expansion | 9.5 10−6Per °F (68-572 F) |
| Density | 0.323 Lb/In3 At 68 F |
| Electrical Conductivity | 9 %IACS @ 68 F |
| Electrical Resistivity | 115.0 Ohms-Cmil/Ft @ 68 F |
| Melting Point – Liquidus | 2100 F |
| Melting Point – Solidus | 2010 F |
| Modulas Of Elasticity In Tension | 18000 Ksi |
| Modulus Of Rigidity | 6800 Ksi |
| Specific Gravity | 8.94 |
| Specific Heat Capacity | 0.09 Btu/Lb/°F At 68 F |
| Thermal Conductivity | 26.0 BTU In/Hr.Ft2.°F @ 68 F |
| HOLLOW RODS | Min Bore Size 20 Mm And Max OD 100 Mm |
| ROUND RODS/RODS | 8mm To 100 Mm |
| HEX | 10mm To 60mm> |
| SQUARE | 10mm To 60mm |
| FLAT | 10mm Min Thickness And Max Width 120mm |
| BILLETS | Up To 200 Mm |
| INGOTS | AS Per Specification |
CuNi6 is a cupro-nickel alloy (CuNi alloy) with low resistivity suitable for use at temperatures up to 300°C (570°F).
Wire in CuNi6 is typically used for low-temperature applications such as heating cables.
| SPECIFICATIONS | DESIGNATION |
| ISO | CuCr1Zr |
| Europen | CuCr1Zr |
| BS | CC 102 |
| Ni % | Cu % | |
| Nominals | 6.0 | Bal. |
| Wire Size | Yield Strength | Tensile Strength | Elongation |
| Ø | Rp0.2 | Rm | A |
| Mm | MPa | Mpa | % |
| 1.00 | 110 | 280 | 30 |
| Density G/Cm3 | 8.9 |
| Electrical Resistivity At 20°C Ω Mm2/M | 0.10 |
| Temperature °C | 20 | 100 | 200 | 300 |
| Ct | 1.00 | 1.06 | 1.11 | 1.19 |
| Temperature °C | 20 |
| W M-1 K-1 | 90 |
| Temperature °C | 20 |
| KJ Kg-1 K-1 | 0.380 |
| Melting Point °C | 1095 |
| Max Continuous Operating Temperature In Air °C | 300 |
| Magnetic Properties | The Material Is Non-Magnetic |
C70600 , Cupro nickel offers excellent corrosion resistance, especially in marine salt water environments. The main, wrought Cupro Nickel alloys chosen for sea water service contain 10 or 30 percent nickel. They also have important additions of iron and manganese which are necessary to maintain good corrosion resistance.
AUTOMOTIVE: Power Steering Tube, Brake Lines
CONSUMER: Screw Lamp Bases
INDUSTRIAL: Condenser Plates, Condensers, Weld Torch Tips, Heat Exchanger Tubes, Valve Bodies, Evaporator Tubes, Pressure Vessels, Distiller Tubes, Pump Impellers for Oil Refining, Ferrules, Evaporators
MARINE: Boat Hulls, Tube Sheet for Salt Water Service, Salt Water Pipe Fittings, Salt Water Piping Systems, Salt Water Piling Wrap, Hot Water Tanks, Salt Water Baffles, Propeller Sleeves, Ship Hulls, Water Hoses
PLUMBING: Flanges
| SPECIFICATIONS | DESIGNATION |
| ISO | CuNi10Fe1Mn |
| Europen | CuNi10Fe1Mn |
| BS | CN 102 |
| JIS | C 7060 |
| Russian | MNZMo10-1-1 |
| Cu | Fe | Pb | Mn | Ni | Zn | |
| Min/Max | Rem | 1.0 – 1.8 | 0.05 | 1 | 9.0 – 11.0 | 1 |
| Nominals | 88.6000 | 1.4000 | – | – | 10.0000 | – |
| Product Property | US Customary |
| Coefficient Of Thermal Expansion | 9.5 10−6Per °F (68-572 F) |
| Density | 0.323 Lb/In3 At 68 F |
| Electrical Conductivity | 9 %IACS @ 68 F |
| Electrical Resistivity | 115.0 Ohms-Cmil/Ft @ 68 F |
| Melting Point – Liquidus | 2100 F |
| Melting Point – Solidus | 2010 F |
| Modulas Of Elasticity In Tension | 18000 Ksi |
| Modulus Of Rigidity | 6800 Ksi |
| Specific Gravity | 8.94 |
| Specific Heat Capacity | 0.09 Btu/Lb/°F At 68 F |
| Thermal Conductivity | 26.0 BTU In/Hr.Ft2.°F @ 68 F |
| HOLLOW RODS | Min Bore Size 20 Mm And Max OD 100 Mm |
| ROUND RODS/RODS | 8mm To 100 Mm |
| HEX | 10mm To 60mm> |
| SQUARE | 10mm To 60mm |
| FLAT | 10mm Min Thickness And Max Width 120mm |
| BILLETS | Up To 200 Mm |
| INGOTS | AS Per Specification |
C71500, Cupro nickel offers excellent corrosion resistance, especially in marine salt water environments. The main, wrought Cupro Nickel alloys chosen for sea water service contain 10 or 30 percent nickel. They also have important additions of iron and manganese which are necessary to maintain good corrosion resistance. Some common applications for Cupro nickel include: valves, and pump components.
INDUSTRIAL: Pump Impellers, Heat Exchanger Tubes, Evaporator Tubes, Distiller Tubes, Condenser Plates, Refrigerators, Process Equipment, Condenser Components, Ferrules, Welding Backing Rings, Flexible Metal Hose, Weld Wire, Boiler Parts, Condensers, Propeller Sleeves, Heat Exchanger Components
MARINE: Salt Water Flanges, Salt Water Piping, Valve Bodies, Sea Water Service, Fittings, Sea Water Condensers, Salt Water Pipe Fittings, Water Boxes – Salt Water Applications, Pump Bodies and Internal Parts-Sea Water
| SPECIFICATIONS | DESIGNATION |
| ISO | CuNi30Mn1Fe |
| Europen | CuNi30Mn1Fe |
| BS | CN 107 |
| JIS | C 7150 |
| Russian | MNZMo30-1-1 |
| Cu | Fe | Pb | Sn | Zn | ||
| Min/Max | Rem | 0.40 – 1.0 | 0.05 | 1 | 29.0 – 33.0 | 1 |
| Nominals | 69.5000 | 0.5000 | – | – | 30.0000 | – |
| Coefficient Of Thermal Expansion | 9.0 10−6Per °F (68-572 F) |
| Density | 0.323 Lb/In3 At 68 F |
| Electrical Conductivity | 4 %IACS @ 68 F |
| Electrical Resistivity | 225.0 Ohms-Cmil/Ft @ 68 F |
| Melting Point Liquid US | 2260 F |
| Melting Point Solid US | 2140 F |
| Modulas Of Elasticity In Tension | 22000 Ksi |
| Modulas Of Rigidity | 8300 Ksi |
| Specific Gravity | 8.94 |
| Specific Heat Capacity | 0.09 Btu/Lb/°F At 68 F |
| Thermal Conductivity | 17.0 BTU In/Hr.Ft2.°F @ 68 F |
| WIRE | 1mm To 8mm |
| HOLLOW RODS | Min Bore Size 20 Mm And Max OD 100 Mm |
| ROUND RODS/RODS | 6mm To 130 Mm |
| HEX | 5mm To 60mm |
| SQUARE | 4mm To 60mm |
| FLAT | 5mm Min Thickness And Max Width 120mm |
| PROFILES / SECTIONS | AS Per Customer Drawing |
| BILLETS | Up To 200 Mm |
| INGOTS | AS Per Specification |